レミンプロとMIペーストプラスが漂白したエナメル質の表面粗さに及ぼす影響

The effect of remin pro and MI paste plus on bleached enamel surface roughness.

• Haleh Heshmat
• Maryam Hoorizad Ganjkar
• Solmaz Jaberi
• Mohammad Javad Kharrazi Fard

抄録

目的:

審美性の向上を求める声の高まりにより，漂白剤の開発が盛んに行われている。歯の硬組織が漂白剤にさらされると，エナメル質の表面の粗さに影響を与える。本研究では，フッ化物やその他の再石灰化剤などのさまざまな表面処理にさらされた漂白したてのエナメル質の表面を評価した．本実験研究の目的は，漂白後のエナメル質表面の粗さに及ぼすカゼインホスホペプチド-アモルファスリン酸カルシウム with Fluoride（MI Paste Plus）とレミンプロの効果を比較することである。

OBJECTIVE: The growing demand for enhanced esthetic appearance has led to great developments in bleaching products. The exposure of hard tissues of the tooth to bleaching agents can affect the roughness of the enamel surface. The freshly bleached enamel surface exposed to various surface treatments such as fluoride and other remineralizing agents have been assessed in this study. The aim of this experimental study was to compare the effect of Casein Phosphopeptide-Amorphous Calcium Phosphate with Fluoride (MI Paste Plus) and Remin Pro on the enamel surface roughness after bleaching.

材料と方法:

本研究のために，健全なヒト永久臼歯のエナメル質サンプル30個を用意した。プロフィロメーターで初期粗さを測定した後，37％過酸化カルバミド漂白剤に20分×2回曝露し，無作為に10名の3群に分けた。グループ1ではCPP-ACPFを含むペースト（MI Paste Plus）を，グループ2ではRemin Proを1日2回，5分間歯に塗布し，15日間経過した。グループ3（コントロール）のサンプルは、人工唾液に15日間浸した。すべてのサンプルの粗さは、開始時、漂白後、研究介入後に測定され、統計的に分析されました。

MATERIALS AND METHODS: Thirty enamel samples of sound human permanent molars were prepared for this study. After initial roughness measurement with profilometer, the samples were exposed to 37% carbamide peroxide bleaching agent 20 minutes twice, and randomly divided into three groups of ten. In group 1, a CPP-ACPF containing paste (MI Paste Plus) and in group 2, Remin Pro were applied to the teeth during a 15 day period for 5 minutes, twice a day. Samples of group 3 (control) were immersed in artificial saliva for 15 days. The roughness of all samples were measured at the beginning, after bleaching and after the study intervention and statistically analyzed.

結果:

表面粗さは，すべての群で漂白後に有意に増加し，Remin ProとCPP-ACPFの両方を塗布した後には，漂白剤を使用した場合に比べて減少した（P<0.005）。Remin ProとCPP-ACPFを使用した後の表面粗さは、統計的に互いに類似していた（P>0.05）。

RESULTS: The surface roughness significantly increased in all groups following bleaching, and then it showed a decrease after application of both Remin Pro and CPP-ACPF in comparison to using bleaching agent (P<0.005). The surface roughness after using Remin Pro and CPP-ACPF was statistically similar to each other (P>0.05).

おわりに:

MI Paste Plus群とRemin Pro群の表面粗さには差がなかった。また，初期のエナメル質の表面粗さに比べて表面粗さは減少した。

CONCLUSION: There was no difference between surface roughness of MI Paste Plus and Remin Pro groups. Also the surface roughness was decreased compared to the initial enamel surface roughness.