レジンセメントのせん断接着強さに及ぼす金属の種類と表面処理の影響（in vitro試験）．

Effect of metal type and surface treatment on shear bond strength of resin cement (in vitro study).

抄録

背景:

レジンボンド固定式部分床義歯は，歯質の過剰な調製を防ぐことができると思われる．金属に対するレジンセメントの接着性を向上させるための表面処理の検討は，これらの修復物の長寿命化に寄与する可能性がある．理想的な調製形態が存在しない可能性があるため，合金の種類とその表面前処理は，最小限の調製量に対する鋳造物の保持力と臨床的に関連性がある可能性がある．

BACKGROUND: Resin-bonded fixed partial dentures appeared to prevent the excessive preparation of dental tissue. Investigation of surface treatments to improve the bond of resin cements to metals may contribute to the longevity of these restorations. Due to the potential lack of ideal preparation form, the type of alloy and its surface pretreatment may have clinically relevant correlations with the retentive strength of castings to minimally retentive preparations.

研究の目的:

本研究の目的は、表面処理による金属合金の種類に応じたレジンセメントの接着強度を検討することである。

AIM: The aim of this search is to study the bonding resin cement strength to different types of the metal alloy due to the surface treatment.

目的:

パラジウム-銀合金（Pb-Ag）および商業用純チタン（CP Ti）鋳造合金とレジンルーティングセメントとのせん断接着強さ（SBS）に及ぼす2種類の表面処理の影響を評価する。

PURPOSE: Evaluate the effects of two different surface treatments on shear bond strength (SBS) between a palladium-silver alloy (Pb-Ag) and commercially pure titanium (CP Ti) cast alloy with resin luting cements.

材料および方法:

直径5 mm，高さ4 mmの円柱120本を，金属の種類によって2つのグループに分けた．母材としてCP Ti Grade I（Tritan-Reintitan-Germany-Dentaurum）60本と貴金属としてPb-Ag（Status-Yamakin, Japan）60本である．各タイプから30本の円柱をアクリル樹脂に埋め込み、残りはアクリル樹脂に埋め込まずに放置した。円筒はすべて炭化ケイ素ペーパーで平滑化し、50μmの酸化アルミニウムでサンドブラストした。各金属の試験片を2つのサブグループに分け，（1）Multilink（Ivoclar Vivadent），（2）Multilink（Ivoclar Vivadent）＋メタルジルコニアプライマー（MZP）のいずれかの合着法を施した．同じ金属の種類と表面処理からなる円柱を2本ごとに接着した．すべての試験片は，蒸留水中に37°Cで24時間保存した後，サーマルサイクリングを行った（500サイクル，5～55°C）．サーマルサイクルの後，試験片は37℃の蒸留水中でさらに24時間保管した後，せん断強度の試験を行った．データ（MPa）は，T-s検定を用いて解析し，グループ間の様々な平均値の有意性を調べ，各2グループ間の比較を行った。

MATERIALS AND METHODS: A total of 120 cylinders having 5 mm in diameter and 4 mm in height were divided into two different main groups of metal type: 60 cylinders cast from CP Ti Grade I (Tritan - Reintitan - Germany-Dentaurum) as a base metal and 60 cylinders cast from Pb-Ag (Status-Yamakin, Japan) as a noble metal. 30 cylinders from each type were embedded in acrylic resin, and the rest were left without embedded in acrylic resin. All of the cylinders were smoothed with silicon carbide papers and sandblasting with 50-μm aluminum oxide. Specimens of each metal type were divided into two subgroups, which received one of the following luting techniques: (1) Multilink (Ivoclar Vivadent), (2) Multilink (Ivoclar Vivadent) plus metal zirconia primer (MZP). Every two cylinders from the same metal type and surface treatment were bonded to each other. All specimens were stored in distilled water at 37°C for 24 h and then thermal cycled (500 cycles, 5-55°C). After thermal cycling, the specimens were stored in 37°C distilled water for an additional 24 h before being tested in shear strength. Data (MPa) were analyzed using T-s tests to study the significance of various - means among groups and perform a comparison between each two groups of them.

結果:

T-s検定により，サンドブラスト法（酸化アルミニウム粒子50μm）とレジンセメント使用前のプライマーMZPの組み合わせは，使用する金属の種類に関係なく，有意な効果を示した（P < 0.05）．金属の種類は，比較したいずれの表面前処理においても，SBSに有意な影響を及ぼさなかった．

RESULTS: The T-s tests indicated significant effect of combination of the sandblasting technique (aluminum oxide particles 50 μm) with the application of primer MZP before using resin cement (P < 0.05) independent of the metal type used. The metal type did not significantly affect SBS for any of the compared surface pretreatments.

結論:

メタルプライマーの塗布は，母材および貴金属に対するSBSを有意に向上させた．剪断強度は合金間で有意差は認められなかった．

CONCLUSION: Metal primer application significantly enhanced SBS to base and a noble metal. No significant differences in shear strength were found between alloys.