7種類のガラスアイオノマー系修復材料の抗菌効果とフッ化物放出量の比較評価．
Comparative Evaluation of Antimicrobial Efficacy and Fluoride Release of Seven Different Glass-Ionomer-Based Restorative Materials.
PMID: 32515423 DOI: 10.3290/j.ohpd.a44140.
抄録
目的:
本研究の目的は、高粘度グラスアイオノマーセメント（EQUIA/GC）1種、レジン変性グラスアイオノマー2種（Fuji II LC/GC、Photac Fil Quick Aplicap/3M Oral Care）、従来型グラスアイオノマー2種（Ketac Molar Easymix/3M、Fuji II/GC）、コンポマー2種（Freedom/SDI、Dyract XP/Dentsply Sirona）について、フッ化物の遊離性と抗菌効果の比較を通じて評価することであった。
PURPOSE: The aim of this study was to evaluate one high-viscosity glass-ionomer cement (EQUIA/GC), two resin-modified glass ionomers (Fuji II LC/GC, Photac Fil Quick Aplicap/3M Oral Care), two traditional glass ionomers (Ketac Molar Easymix/3M, Fuji II/GC), and two compomers (Freedom/SDI, Dyract XP/Dentsply Sirona) through a comparison of fluoride release and antimicrobial effects.
材料と方法:
フッ化物遊離量は7種類の試料を各10個、抗菌効果試験は各20個の試料を用意し、合計210個の試料を作成した。フッ化物放出量の測定は、試料に蒸留水５ｍｌとＴＩＳＡＢⅡ５ｍｌを加え、３７℃でインキュベートした。1日目、3日目、7日目、14日目、28日目に選択イオン電極を用いてフッ化物濃度を測定した。抗菌効果を比較するために、20個のサンプルを2つのグループに分け、ストレプトコッカス・ミュータンス菌とラクトバチルス・アシドフィルス菌を含む培地に移植した。測定は２日目、４日目、６日目に行った。阻害領域の直径はミリメートル（ｍｍ）で記録した。
MATERIALS AND METHODS: A total of 210 samples were prepared, as 10 for each of the 7 materials for fluoride release and 20 for each material for the antimicrobial effect tests. To measure fluoride release, 5 ml distilled water and 5 ml TISAB II were added to the samples, which were then incubated at 37˚C. The fluoride levels of the material were measured using the selective ion electrode on days 1, 3, 7, 14 and 28. To compare the antimicrobial effects, 20 samples were divided in two groups and implanted in culture media containing Streptococcus mutans and Lactobacillus acidophylus. Measurements were taken on days 2, 4 and 6. The diameter of the inhibition zone was recorded in millimetre (mm).
結果:
すべての材料はフッ化物を放出し，その差は統計的に有意であった(p < 0.01)．S. mutansおよびL. acidophylusに対する抗菌効果を評価したところ、すべての測定日において統計的に有意な差が認められた。
RESULTS: All the materials released fluoride and the difference between them was determined to be statistically significant (p < 0.01). The antimicrobial effect values of the materials against S. mutans and L. acidophylus were evaluated and statistically significant difference was determined between the materials on all the measurement days.
結論:
すべての材料でフッ化物の放出が観察された。その結果，コンポマーを除くすべての材料がS. mutansおよびL. acidophylusに対して抗菌効果を示した．キーワード：フッ化物，グラスアイオノマー，抗菌性，S.ミュータンス菌，L.アシドフィラス菌
CONCLUSIONS: All the materials were observed to release fluoride. With the exception of the compomers, all the other materials showed an antimicrobial effect against S. mutans and L. acidophylus. Key words: fluoride, glass ionomer, antimicrobial, S. mutans, L. acidophylus.