High Performance Poly-etheretherketone Removable Partial Denture Frameworks constructed by Various Techniques (Study)の保持力評価．

Retention Assessment of High Performance Poly-etheretherketone Removable Partial Denture Frameworks Constructed by Various Techniques ( Study).

抄録

問題の提起:

ポリエーテルエーテルケトンは、金属フレームの代わりに取り外し可能な部分義歯のフレームワークの構築に使用される新しい材料である。この材料は、様々な方法で製造することができる。最も一般的な方法は、射出成形やCAD/CAM（Computer Aided Design/Computer Aiding Manufacturing）によるミリング技術です。製作技術は、保持力に影響を与えることにより、フレームワークの適合性に影響を与える可能性がある。

Statement of the Problem: Poly-etheretherketone is a novel material used in the construction of the removable partial dentures frameworks instead of the metal frameworks. This material can be fabricated by various techniques. Most common methods are the injection molding or Computer Aided Design/Computer Aiding Manufacturing (CAD/CAM) milling techniques. The fabrication technique may affect the adaptation of the frameworks by influencing the retention.

目的:

高性能ポリエーテルエーテルケトンの射出成形（プレス）またはCAD/CAMミリングによる加工技術が，ケネディ上顎分類のリハビリテーション用可撤式部分床義歯のフレーム保持力に及ぼす影響を評価する．

Purpose: To assess the effect of the processing techniques of high performance Poly-etheretherketone either by injection molding (pressing) or CAD/CAM milling techniques on removable partial denture frameworks retention for rehabilitation of upper class I Kennedy classification.

材料と方法:

本研究は、第一小臼歯から第一小臼歯までの天然歯を有する部分無歯顎弓のエポキシ樹脂模型を用いて行った。第一小臼歯と犬歯には、0.50mmの中間頬側のリテンティブアンダーカット、ディスタルガイドプレーン、第一小臼歯にはメシアルオクルーザルレストシート、犬歯にはシンギュラムレストシートを施したポーセレンフュージョンメタルクラウンを装着するために縮小した。フレームの構築方法を考慮して，20個のサンプルを2つのグループに分けた。I群では10個のフレームワークを射出成形で作製し，II群では10個のフレームワークをCAD/CAMで作製した。取り外しと挿入は，両グループとも，それぞれ120，720，1440サイクルで行った。リテンション値は、サイクル前と各インターバル後にユニバーサル・テスト・マシンを用いて測定した。

Materials and Method: This study was performed on one epoxy resin model representing the partially edentulous maxillary arch with natural teeth extending from first premolar to first premolar. First premolars and canines were reduced to receive porcelain fused to metal crowns with 0.50mm mesio-buccal retentive undercuts, distal guiding planes and mesial occlusal rest seat on first premolars and cingulum rest seat on canines. Considering the construction technique of frameworks, twenty samples were divided into two groups. In the group I, ten frameworks were fabricated by injection molding, and in the group II, ten frameworks were fabricated by CAD/CAM. The removal and insertion was carried out at 120, 720 and 1440 cycles for both groups, respectively. The retention values were measured by using Universal Testing Machine before cycling and after each interval.

結果:

独立したt-testにより、異なるシミュレーションサイクルにおける保持力について、両群間で有意差が認められた。一方、各群の異なるサイクルでの保持力をペアサンプルt-testで比較したところ、サイクルの最後まで保持力が有意に減少した（<0.001）。

Results: Independent t-test showed significant difference on retention at different simulation cycles between groups. Group II exhibited significantly less retention than group I (< 0.001), while comparing the retention at different cycles within each group by paired sample t-test exhibited significant decrease of retention till the end of the cycling (< 0.001).

結論:

保持力の観点から見ると，射出成形法で作製した高性能ポリエーテルエーテルケトンフレームは，CAD/CAM技術を用いたミリング法よりも有望な方法である。

Conclusion: From the retention point of view, high performance poly-etheretherketone frameworks fabricated by injection molding technique provided a promising method over CAD/CAM technique milling method.