光硬化中のレジンマトリックスコンポジットの光透過率に及ぼす無機フィラーの影響：統合的レビュー

The influence of inorganic fillers on the light transmission through resin-matrix composites during the light-curing procedure: an integrative review.

抄録

目的:

本研究の目的は，光硬化中のレジンマトリックスコンポジットの光透過率に及ぼす無機フィラーの影響について，統合的な検討を行うことである．

PURPOSE: The objective of this study was to perform an integrative review on the effect the inorganic fillers on the light transmission through the resin-matrix composites during the light-curing procedure.

方法:

PubMed で以下の検索語を用いて文献調査を行った．「フィラー」または「粒子」および「光硬化」または「重合」および「光透過」または「光吸収」または「光照射」または「光減衰」または「光拡散」および「樹脂複合材料」。検索対象は、過去10年以内に英語で発表された論文である。

METHOD: A bibliographic review was performed on PubMed using the following search terms: "fillers" OR "particle" AND "light curing" OR "polymerization" AND "light transmission" OR "light absorption" OR "light irradiance" OR "light attenuation" OR "light diffusion" AND "resin composite." The search involved articles published in English language in the last 10 years.

結果:

従来のレジンマトリックスコンポジットの二軸強度と硬度が重合深度の関数として減少することを報告した研究がある。しかし，バルクフィル™複合材料では，重合深さによる2軸強度と硬度の有意差は認められなかった．強度および硬度は，無機充填材のサイズと含有量を増加させることによって向上したが，シリカ粒子サイズの増加に伴って転化度が徐々に低下することを示した研究もある．ガラスセラミック球状フィラーの透光性は，主にレジン-マトリックス複合材料の深部近接領域のような臨界状態において光拡散を促進した．

RESULTS: Selected studies reported a decrease in biaxial strength and hardness in traditional resin-matrix composites in function of the depth of polymerization. However, there were no significant differences in biaxial strength and hardness recorded along the polymerization depth of Bulk-Fill™ composites. Strength and hardness were enhanced by increasing the size and content of inorganic fillers although some studies revealed a progressive decrease in the degree of conversion on increasing silica particle size. The translucency of glass-ceramic spherical fillers promoted light diffusion mainly in critical situations such as in the case of deep proximal regions of resin-matrix composites.

結論:

レジン-マトリックスコンポジットの透過光量は，無機フィラー粒子のサイズ，含有量，微細構造，および形状に影響される．変換度の低下は，樹脂-マトリックス複合体の物理的および機械的特性に悪影響を及ぼす．

CONCLUSIONS: The amount of light transmitted through the resin-matrix composites is influenced by the size, content, microstructure, and shape of the inorganic filler particles. The decrease of the degree of conversion affects negatively the physical and mechanical properties of the resin-matrix composites.

臨床的関連性:

樹脂基複合材料の化学組成に含まれる無機フィラーの種類と含有量は，その重合性に影響を及ぼす．その結果、樹脂基材複合材料の臨床性能が低下し、物性の変化や劣化を招くことがある。樹脂基材複合体の化学組成に含まれる無機充填材の種類によって，樹脂基材複合体の重合様式を改善することができる．

CLINICAL RELEVANCE: The type and content of inorganic fillers in the chemical composition of resin-matrix composites do affect their polymerization. As a consequence, the clinical performance of resin-matrix composites can be compromised leading to variable physical properties and degradation. The polymerization mode of resin-matrix composites can be improved according to the type of inorganic fillers in their chemical composition.