5Y-ZPジルコニア、3-YTZPジルコニア、および二ケイ酸リチウムの透光性パラメータと接着強度の比較

Comparison of the translucency parameters and bond strength of 5Y-ZP zirconia, 3-YTZP zirconia, and lithium disilicate.

抄録

背景:

E-maxは従来のジルコニアよりも審美性に優れた材料である。また、従来のジルコニアと接着性セメントとの接着強度は低い。新世代ジルコニアである5-YZPの審美性や接着強度が、e-maxや従来のジルコニアと比較してどうなのかについては、十分な研究がなされていない。5-YZPは審美性と接着強度の点でe-maxの代替となり得るか？

BACKGROUND: E-max is a more aesthetic material than traditional zirconia. In addition, the bond strength of traditional zirconia with adhesive cements is lower. There are not enough studies on how the aesthetic values and bond strength of 5-YZP, the new generation zirconia, compare to e-max and traditional zirconia. Can 5-YZP be an alternative to e-max in terms of aesthetics and bond strength?

研究の目的:

本研究の目的は、5y-zpジルコニアと旧世代ジルコニアおよび二ケイ酸リチウムとの透光特性および接着能力を比較することである。

AIM: The aim of the study is to compare the translucency property and bonding ability of 5y-zp zirconias with previous generation zirconias and lithium disilicate.

材料と方法:

透光性を測定するために2種類のジルコニアKatana UTとKatana HT、および一種類の二ケイ酸リチウムIPS e.max CAD LTを用い、3つのグループを形成した（n = 10）。透光性試験片を作製した（n = 10）。分光光度計で白黒を背景にL*a*b*値を測定し、DE00を算出した。微小剪断試験を行うために、ジルコニアとIPS e.max CADブロックから円柱のデザインを作製した（n = 20）。試料を熱サイクルによってエージングした後、2つの異なる接着性セメントシステムで抜去歯にセメント固定した試料に微小せん断試験を適用した。

MATERIALS AND METHODS: Two types of zirconia Katana UT and Katana HT for measuring translucency values; and using a type of lithium disilicate IPS e.max CAD LT, three groups were formed (n = 10). Translucency specimens were fabricated (n = 10). Their L*a*b* values were measured against a black-and-white background with a spectrophotometer, and DE00 was calculated. To perform micro-shear tests, a cylinder design was made from zirconia and IPS e.max CAD blocks (n = 20). After the samples were aged by thermal cycle, the micro-shear test was applied to specimens cemented to teeth extracted with two different adhesive cement systems.

結果:

一元配置分散分析の結果、各群の半透明性パラメータ（TP）値の間に統計的に有意な差が認められた。Tukeyの正直有意差（HSD）の多重比較によると、3群の値は統計的に互いに異なっていた。IPS e.max CAD群のTP値が最も高かったが、Katana HT群のTP値は最も低かった。

RESULTS: According to the results of one-way analysis of variance, a statistically significant difference was found between the translucency parameter (TP) values of the groups. According to Tukey's honestly significant difference (HSD) multiple comparisons, the values of the three groups are statistically different from each other. Although IPS e.max CAD group has the highest TP values, the Katana HT group has the lowest values.

結論:

5Y-PZのTPは、3Y-TZPと二ケイ酸リチウムの中間の値であった。3Y-TZPと5Y-ZPの長期接合強度は、二ケイ酸リチウムと同程度であった。前歯部においてガラスセラミックの代替となるためには、透光性と接着強度の値を改善する必要がある。

CONCLUSION: 5Y-PZ has a TP intermediate to those of 3Y-TZP and lithium disilicate. Long-term bond strength of 3Y-TZP and 5Y-ZP were similar to those of lithium disilicate. To be an alternative to glass ceramics in the anterior region, translucency and bond strength values need to be improved.